Estimation of interfacial fracture toughness based on progressive edge delamination of a thin transparent coating on a polymer substrate

2010

Evaluation of interfacial toughness of sub-micron-thickness layers deposited on a ductile substrate is a challenging task which has motivated different experimental approaches Fragmentation testing was used in the present study as a means of interface characterization of a silicon-nitride-coated polyimide substrate. During the test, after an initial rapid segmentation-cracking phase, the coating fragments developed edge delaminations which propagated in a stable manner with further increase in the applied strain The debonding process was modelled by the finite element method Incorporating a cohesive zone at the front of the interfacial crack The edge cracks were found to be dominated by mod…